High-quality carbon structural steel, alloy structural steel, and stainless heat-resistant steel seamless steel pipe for high-pressure and above steam boiler pipes in GB/T5310-2017 standard.The steel pipe is required to have high endurance strength, high anti-oxidation and corrosion performance, and good structural stability.Material mainly is Cr-Mo alloy and Mn Alloy, Such as 20G, 20MnG, 20MoG, 12CrMoG, etc

Payment: 30% deposit, 70% L/C or B/L copy or 100% L/C at sight

Min.Order Quantity: 1 PC

Supply Ability: Annual 20000 Tons Inventory of Steel Pipe

Lead Time: 7-14 days if in stock, 30-45 days to produce

Packing: Black Vanishing, bevel and cap for every single pipe; OD below 219mm need to pack in bundle, and each bundle no exceed 2 tons.

Send email to us Download as PDF

Product Detail

Product Tags

Application

Mainly used for high pressure and high temperature service of boiler(Superheater tube, reheater tube, air guide tube, main steam tube for high and ultra high pressure boilers). Under the action of high temperature flue gas and water vapor, the tube will oxidize and corrode. It is required that the steel pipe has high durability, high resistance to oxidation and corrosion, and good structural stability.

Main Grade

Grade of high-quality carbon structural steel: 20g、20mng、25mng

Grade of alloy structural steel: 15mog、20mog、12crmog、15crmog、12cr2mog、12crmovg、12cr3movsitib, etc

In different standard there are different Grade

GB5310 : 20G = EN10216 P235GH

Material

P235GH

≤0.16

≤0.35

≤1.20

≤0.025

≤0.3

≤0.08

≤0.3

≤0.02

≤0.3

≤0.04

≤0.02

20G

0.17-0.24

0.17-0.37

0.35-0.65

≤0.03

Material	Tensile Strength	Yield	Extension
20G	410-550	≥245	≥24
P235GH	320-440	215-235	27
P235GH	360-500	215-235	25

Material	Test
20G：	Flattening	Hydraulic	Impact Test	NDT	Eddy	Grazin size	Microscopic structure
P235GH	Flattening	Hydraulic	Impact Test	NDT	Electromagnetic	Drift expanding	Leak tightness

Tolerance

Wall Thickness and Outter Diameter:

If there is no special requirements, pipe gonna be delivery as norminal outter diameter and norminal wall thickness. As follow sheet

Classification designation	Method of manufacture	Size of pipe			Tolerance
					Normal grade	High grade
W H	Hot Rolled（extrude） pipe	Norminal outter Diameter （D）	<57		士 0.40	±0,30
			57 〜325	SW35	±0.75%D	±0.5%D
				S>35	±1%D	±0.75%D
			>325 〜6。。		+ 1%D or + 5.Take lesser one一2
			>600		+ 1%D or + 7,Take lesser one一2
		Norminal Wall Thickness （S）	<4.0		±\|・丨）	±0.35
			>4.0-20		+ 12.5%S	±10%S
			>20	DV219	±10%S	±7.5%S
				心219	+ 12.5%S -10%S	土 10%S

W-H	Thermal expansion pipe	Norminal outter Diameter (D)	all	±1%D	±0.75%。
W-H	Thermal expansion pipe	Norminal Wall Thickness (S)	all	+ 20%S -10%S	+ 15%S -io%s
W-C	Cold drawn(rolled) Ppipe	Norminal outter Diameter (D)	<25.4	±'L1j	—
			>25.4 〜4()	±0.20
			>40 〜50	\|:0.25	—
			>50 〜60	±0.30
			>60	±0.5%D
		Norminal Wall Thickness (S)	<3.0	±0.3	±0.2
		Norminal Wall Thickness (S)	>3.0	S	±7.5%S

Length:

The usual length of steel pipes is 4 000 mm ~ 12 000 mm. After consultation between the supplier and the buyer, and fill in the contract, it can be delivered steel pipes with a length greater than 12 000 mm or shorter than I 000 mm but not shorter than 3 000 mm; short length The number of steel pipes less than 4,000 mm but not less than 3,000 mm shall not exceed 5% of the total number of steel pipes delivered

Delivery weight：
When the steel pipe is delivered according to the nominal outer diameter and nominal wall thickness or the nominal inner diameter and nominal wall thickness, the steel pipe is delivered according to the actual weight. It can also be delivered according to the theoretical weight.
When the steel pipe is delivered according to the nominal outer diameter and minimum wall thickness, the steel pipe is delivered according to the actual weight; the supply and demand parties negotiate. And it is indicated in the contract. The steel pipe can also be delivered according to the theoretical weight.

Weight tolerance：
According to the requirements of the purchaser, after consultation between the supplier and the purchaser, and in the contract, the deviation between the actual weight and the theoretical weight of the delivery steel pipe shall meet the following requirements:
a) Single steel pipe: ± 10%;
b) Each batch of steel pipes with a minimum size of 10 t: ± 7.5%.

Test Requirement

Hydraustatic Test:

The steel pipe should be tested hydraulically one by one. The maximum test pressure is 20 MPa. Under the test pressure, the stabilization time should be not less than 10 s, and the steel pipe should not leak.

After the user agrees, the hydraulic test can be replaced by eddy current testing or magnetic flux leakage testing.

Nondestructive Test：

Pipes that require more inspection should be ultrasonically inspected one by one. After the negotiation requires the consent of the party and is specified in the contract, other non-destructive testing can be added.

Flattening Test：

Tubes with an outer diameter greater than 22 mm shall be subjected to a flattening test. No visible delamination, white spots, or impurities should occur during the entire experiment.

Flaring Test:

According to the requirements of the purchaser and stated in the contract, the steel pipe with outer diameter ≤76mm and wall thickness ≤8mm can be done flaring test . The experiment was performed at room temperature with a taper of 60 °. After the flaring, the flaring rate of the outer diameter should meet the requirements of the following table, and the test material must not show cracks or rips

Steel Type	Outter diameter flaring rate of steel pipe/%
	Inner Diameter/Outter Diameter
	<0.6	>0.6 〜0.8	>0.8
High-quality carbon structural steel	10	12	17
Structural alloy steel	8	10	15
•The inner diameter is calculated for the sample.