케이스에 대한 사양 및 튜브 API 사양 5CT NINTH EDITION-2012

간단한 설명:

Api5ct oil casing is mainly used to transport oil, natural gas, gas, water and other liquids and gases,It can be divided into seamless steel pipe and welded steel pipe. Welded steel pipe mainly refers to longitudinal welded steel pipe


  • Payment: 30% deposit, 70% L/C or B/L copy or 100% L/C at sight
  • Min.Order Quantity: 1 PC
  • Supply Ability: Annual 20000 Tons Inventory of Steel Pipe
  • Lead Time: 7-14 days if in stock, 30-45 days to produce
  • Packing: Black Vanishing, bevel and cap for every single pipe; OD below 219mm need to pack in bundle, and each bundle no exceed 2 tons.
  • 제품 상세 정보

    자주하는 질문

    제품 태그

    개요

    표준 : API를 5CT

    학년 그룹 : J55, K55, N80, L80, P110 등

    두께 : 1~1백mm

    외경 (라운드) : 10-1,000밀리미터

    길이 : R1, R2, R3

    섹션 모양 : 라운드

    기원의 장소 : 중국

    증명서 : ISO9001 : 2008

     

    합금 여부 : 없음

    응용 프로그램 : 기름칠 및 케이싱 파이프

    표면 처리 : 고객의 요구 사항으로

    기술 : 열간 압연

    열처리 : 담금질 및 정규화

    특수 파이프 : 짧은 공동

    사용법 : 기름칠 및 가스

    테스트 : NDT

    신청

    Pipe in Api5ct is mainly used for drilling of oil and gas wells and transportation of oil and gas. Oil casing is mainly used to support the borehole wall during and after the completion of the well to ensure the normal operation of the well and the completion of the well.

    홈페이지 등급

    학년 : J55, K55, N80, L80, P110 등

    화학 구성 요소

     

    등급 유형 망간 CR 니켈 구리 에스
    최대 최대 최대 최대 최대 최대 최대 최대 최대
    1 2 3 4 5 6 7 8 9 10 11 12 13 14 15
    H40 - - - - - - - - - - - - 0.030 -
    J55 - - - - - - - - - - - - 0.030 -
    K55 - - - - - - - - - - - - 0.030 -
    N80 1 - - - - - - - - - - 0.030 0.030 -
    N80 - - - - - - - - - - 0.030 0.030 -
    R95 - - 0.45 C - 1.90 - - - - - - 0.030 0.030 0.45
    L80 1 - 0.43 - 1.90 - - - - 0.25 0.35 0.030 0.030 0.45
    L80 9Cr - 0.15 0.3 0.60 0 90 1.10 8.00 10.0 0.50 0.25 0.020 0.030 1.00
    L80 13Cr 0.15 0.22 0.25 1.00 - - 12.0 14.0 0.50 0.25 0.020 0.030 1.00
    C90 1 - 0.35 - 1.20 0.25 B 0.85 - 1.50 0.99 - 0.020 0.030 -
    T95 1 - 0.35 - 1.20 0.25 B 0.85 0 ~ 40 1.50 0.99 - 0 020 0.010 -
    C110 - - 0.35 - 1.20 0.25 1.00 0.40 1.50 0.99 - 0.020 0.005 -
    P1I0 이자형 - - - - - - - - - 0.030 전자 0.030 전자 -
    QI25 1 - 0.35 1.35 - 0.85 - 1.50 0.99 - 0.020 0.010 -
    보여 주 요소는 제품 분석에보고해야한다
    제품이 오일 켄칭 또는 중합체 켄칭 경우 L80의 탄소 함량이 0.50 %에서 최대까지 증가 될 수있다.
    벽 두께가 17.78 mm 미만이면 B 급 C90 타입 1의 몰리브덴 함량은 최소 허용 오차가 없다.
    제품이 오일 켄칭 경우 C R95의 탄소 CONTECT 0.55 %의 최대까지 증가 될 수있다.
    벽 두께가 작은 17.78 mm를 초과하는 경우 라 T95 타입 1의 몰리브덴의 함유량은 0.15 % 최소로 감소 될 수있다.
    예를 들어 급 EW P110은 인의 함유량이 0.020 %의 최대 및 황 함량 0.010 % 최대한다.

    기계적 성질

     

    등급

    유형

    총 신장에서로드

    항복 강도
    MPA는

    인장 강도

    MPA는

    경도 A, C의
    최대

    지정된 벽 두께

    허용 경도 대안 (B)

     

     

     

     

     

     

     

     

     

     

     

    최대

     

    HRC

    HBW

    mm

    HRC

    H40

    -

    0.5

    276

    552

    414

    -

    -

    -

    -

    J55

    -

    0.5

    379

    552

    517

    -

    -

    -

    -

    K55

    -

    0.5

    379

    552

    655

    -

    -

    -

    -

    N80

    1

    0.5

    552

    758

    689

    -

    -

    -

    -

    N80

    0.5

    552

    758

    689

    -

    -

    -

    -

    R95

    -

    0.5

    655

    758

    724

    -

    -

    -

    -

    L80

    1

    0.5

    552

    655

    655

    23.0

    241.0

    -

    -

    L80

    9Cr

    0.5

    552

    655

    655

    23.0

    241.0

    -

    -

    L80

    l3Cr

    0.5

    552

    655

    655

    23.0

    241.0

    -

    -

    C90

    1

    0.5

    621

    724

    689

    25.4

    255.0

    ≤12.70

    3.0

    12.71-19.04

    4.0

    19.05-25.39

    5.0

    ≥25.4

    6.0

    T95

    1

    0.5

    655

    758

    724

    25.4

    255

    ≤12.70

    3.0

    12.71-19.04

    4.0

    19.05-25.39

    5.0

    ≥25.4

    6.0

    C110

    -

    0.7

    758

    828

    793

    30.0

    286.0

    ≤12.70

    3.0

    12.71-19.04

    4.0

    19.05-25.39

    5.0

    ≥25.4

    6.0

    P110

    -

    0.6

    758

    965

    862

    -

    -

    -

    -

    Q125

    1

    0.65

    862

    1034

    931

    (B)

    -

    ≤12.70

    3.0

    12.71-19.04

    4.0

    19.05

    5.0

    a 분쟁에서 케이스 실험실 록웰 C 경도 시험 옐로 방법으로 사용한다.
    (B) 없음 경도 범위가 지정되지 않지만 최대 편차는 7.8 및 7.9에 따라 제조 대조군으로 제한된다.
     등급 L80 (모든 유형), C90, C110 및 T95의 경도 시험은, 요구가 HRC 스케일에 기재된 관통 벽은 최대 평균 경도 번호이다.

    테스트 요구 사항

    화학 조성과 기계적 성질을 확보 이외에도, 정압 시험 하나씩 수행하고, 벌어짐 평탄화 테스트가 수행된다. . 또한, 완성 된 강관의 미세 결정립 크기, 탈탄 층에 대한 특정 요구 사항이있다.

    Tensile Test:

    1. For the steel material of the products, manufacturer should perform tensile test. For the elecrtrice welded pipe, depondeds on manufacturer's choice, tensile test can be performed on the steel plate that used to make pipe or perfomred on steel pipe directly. An test performed on a product can also be          used as a product test.

    2. The test tubes shall be randomly selected. When multiple tests are required, the sampling method shall ensure that the samples taken can represent the beginning and end of the heat treatment cycle (if applicable) and both ends of the tube. When multiple tests are required, the pattern shall be taken from different tubes except that the thickened tube sample may be taken from both ends of a tube.

    3. The seamless pipe sample can be taken at any position on the circumference of the pipe; the welded pipe sample should be taken at about 90 ° to the weld seam, or at the option of the manufacturer. Samples are taken at about a quarter of the strip width.

    4. No matter before and after the experiment, if the sample preparation is found to be defective or there is a lack of materials irrelevant to the purpose of the experiment, the sample may be scrapped and replaced with another sample made from the same tube.

    5. If a tensile test representing a batch of products does not meet the requirements, the manufacturer may take another 3 tubes from the same batch of tubes for re-inspection.

    If all the retests of the samples meet the requirements, the batch of tubes is qualified except the unqualified tube that was originally sampled.

    If more than one sample is initially sampled or one or more samples for retesting do not meet the specified requirements, the manufacturer may inspect the batch of tubes one by one.

    The rejected batch of products can be reheated and reprocessed as a new batch.

    Flattening Test:

    1. The test specimen shall be a test ring or end cut of not less than 63.5mm (2-1 / 2in).

    2. Specimens may be cut before heat treatment, but subject to the same heat treatment as the pipe represented. If a batch test is used, measures shall be taken to identify the relationship between the sample and the sampling tube. Each furnace in each batch should be crushed.

    3. The specimen shall be flattened between two parallel plates. In each set of flattening test specimens, one weld was flattened at 90 ° and the other flattened at 0 °. The specimen shall be flattened until the tube walls are in contact. Before the distance between the parallel plates is less than the specified         value, no cracks or breaks should appear in any part of the pattern. During the entire flattening process, there should be no poor structure, welds not fused, delamination, metal overburning, or metal extrusion.

    4. No matter before and after the experiment, if the sample preparation is found to be defective or there is a lack of materials irrelevant to the purpose of the experiment, the sample may be scrapped and replaced with another sample made from the same tube.

    5. If any sample representing a tube does not meet the specified requirements, the manufacturer may take a sample from the same end of the tube for supplementary testing until the requirements are met. However, the length of the finished pipe after sampling must not be less than 80% of the original        length. If any sample of a tube representing a batch of products does not meet the specified requirements, the manufacturer may take two additional tubes from the batch of products and cut the samples for re-testing. If the results of these retests all meet the requirements, the batch of tubes is                      qualified except for the tube originally selected as the sample. If any of the retest samples does not meet the specified requirements, the manufacturer may sample the remaining tubes of the batch one by one. At the option of the manufacturer, any batch of tubes can be re-heat treated and retested as a      new batch of tubes.

    Impact Test:

    1. For tubes, a set of samples shall be taken from each lot (unless documented procedures have been shown to meet regulatory requirements). If the order is fixed at A10 (SR16), the experiment is mandatory.

    2. For casing, 3 steel pipes should be taken from each batch for experiments. The test tubes shall be randomly selected, and the sampling method shall ensure that the samples provided can represent the beginning and end of the heat treatment cycle and the front and back ends of the sleeve during heat        treatment.

    3. Charpy V-notch impact test

    4. No matter before and after the experiment, if the sample preparation is found to be defective or there is a lack of materials irrelevant to the purpose of the experiment, the sample may be scrapped and replaced with another sample made from the same tube. Specimens should not be simply judged              defective simply because they do not meet the minimum absorbed energy requirements.

    5. If the result of more than one sample is lower than the minimum absorbed energy requirement, or the result of one sample is lower than 2/3 of the specified minimum absorbed energy requirement, three additional samples shall be taken from the same piece and retested. The impact energy of each          retested specimen shall be greater than or equal to the specified minimum absorbed energy requirement.

    6. If the results of a certain experiment do not meet the requirements and the conditions for the new experiment are not met, then three additional samples are taken from each of the other three pieces of the batch. If all the additional conditions meet the requirements, the batch is qualified except the          one that failed initially. If more than one additional inspection piece does not meet the requirements, the manufacturer may choose to inspect the remaining pieces of the batch one by one, or reheat the batch and inspect it in a new batch.

    7. If more than one of the initial three items required to prove a batch of qualifications are rejected, re-inspection is not allowed to prove the batch of tubes is qualified. The manufacturer may choose to inspect the remaining batches piece by piece, or reheat the batch and inspect it in a new batch.

    Hydrostatic Test:

    1. Each pipe shall be subjected to hydrostatic pressure test of the whole pipe after thickening (if appropriate) and final heat treatment (if appropriate), and shall reach the specified hydrostatic pressure without leakage. The experimental pressure holding time was made up less than 5s. For welded pipes,        the welds of the pipes shall be checked for leaks under test pressure. Unless the whole pipe test has been performed at least in advance at the pressure required for the final pipe end condition, the thread processing factory should perform a hydrostatic test (or arrange such a test) on the whole pipe.

    2. Pipes to be heat treated shall be subjected to a hydrostatic test after the final heat treatment. The test pressure of all pipes with threaded ends shall be at least the test pressure of threads and couplings.

    3 .After processing to the size of the finished flat-end pipe and any heat-treated short joints, the hydrostatic test shall be performed after the flat end or the thread.

    Tolerance

    Outter Diameter:

    Range Tolerane
    <4-1/2 ±0.79mm(±0.031in)
    ≥4-1/2 +1%OD~-0.5%OD

    For thickened joint joint tubing with a size smaller than or equal to 5-1 / 2, the following tolerances apply to the outer diameter of the pipe body within a distance of approximately 127mm (5.0in) next to the thickened part; The following tolerances apply to the outer diameter of the tube within a distance of approximately equal to the diameter of the tube immediately adjacent to the thickened portion.

    Range Tolerance
    ≤3-1/2 +2.38mm~-0.79mm(+3/32in~-1/32in)
    >3-1/2~≤5 +2.78mm~-0.75%OD(+7/64in~-0.75%OD)
    >5~≤8 5/8 +3.18mm~-0.75%OD(+1/8in~-0.75%OD)
    >8 5/8 +3.97mm~-0.75%OD(+5/32in~-0.75%OD)

    For external thickened tubing with a size of 2-3 / 8 and larger, the following tolerances apply to the outer diameter of the pipe that is thickened and the thickness gradually changes from the end of the pipe

    Rang Tolerance
    ≥2-3/8~≤3-1/2 +2.38mm~-0.79mm(+3/32in~-1/32in)
    >3-1/2~≤4 +2.78mm~-0.79mm(+7/64in~-1/32in)
    >4 +2.78mm~-0.75%OD(+7/64in~-0.75%OD)

    Wall Thickness:

    The specified wall thickness tolerance of the pipe is -12.5%

    Weight:

    The following table is the standard weight tolerance requirements. When the specified minimum wall thickness is greater than or equal to 90% of the specified wall thickness, the upper limit of the mass tolerance of a single root should be increased to + 10%

    Quantity Tolerance
    Single Piece +6.5~-3.5
    Vehicle Load Weigh≥18144kg(40000lb) -1.75%
    Vehicle Load Weigh<18144kg(40000lb) -3.5%
    Order Quantity≥18144kg(40000lb) -1.75%
    Order Quantity<18144kg(40000lb) -3.5%